Non Reciprocal Passive Components on LTCC Ferrite Substrate

It appears your Web browser is not configured to display PDF files. Download adobe Acrobat or click here to download the PDF file.

Click here to download the PDF file.

Creator: 

Yang, Shicheng

Date: 

2016

Abstract: 

This thesis investigates passive components (mainly circulators) based on ferrite LTCC substrate. The external magnets used in conventional circulators must be strong to overcome the ferrite's demagnetization factor. The novel circulator presented herein uses an embedded winding within the ferrite to magnetize the material from the inside, thereby significantly reducing the demagnetization effects. Because of the controllability of the bias field, the resulting device is also multifunctional: when the windings are energized by a current, the device operates as a dynamic circulator in which the circulation direction can be changed by switching the direction of the current. If an external magnet is placed on the circulator, its operating frequency can be changed by adjusting the bias current. Unlike other LTCC circulators with external magnets, the proposed device can even operate as a power splitter by removing the bias current. A circulator prototype has been characterized in three states: unbiased, biased by windings and biased by windings and external magnets. When no current is applied, the transmission of each port is about -5 dB with return loss better than 20 dB at 14.8 GHz. When a current of 300 mA is injected into the windings, the measured insertion loss and isolation of the circulator are approximately 3 dB and 8 dB, respectively, whereas the return loss is better than 20 dB at 14.2 GHz. When external magnets are added in addition to the current of 200 mA, the insertion loss and isolation improve to 1.6 dB and 23 dB, respectively at 14.2 GHz. The variation of the circulator's working frequency is 0.6 GHz. This is achieved firstly by the change of internal magnetization M when current is less than 120 mA, then the heat due to the winding increases the ferrite's μeff leading to more frequency shifting. The total size (L*W*H) is 8mm*8mm*1.1mm.

Subject: 

Engineering - Electronics and Electrical

Language: 

English

Publisher: 

Carleton University

Thesis Degree Name: 

Doctor of Philosophy: 
Ph.D.

Thesis Degree Level: 

Doctoral

Thesis Degree Discipline: 

Engineering, Electrical and Computer

Parent Collection: 

Theses and Dissertations

Items in CURVE are protected by copyright, with all rights reserved, unless otherwise indicated. They are made available with permission from the author(s).