Directly photoinscribed refractive index change and Bragg gratings in Ohara WMS-15 glass ceramic.


  • Krug, Peter A.
  • Rogojan, Rodica Matei
  • Albert, Jacques




We inscribed thick volume gratings in WMS-15 glass ceramic by ultraviolet light at 193 and 248 nm. Unlike earlier work in ceramic materials, the inscription process modified the optical properties of the material without the need for any additional chemical or thermal processing. Experimental evidence from measurements of grating growth, thermal annealing, and spectral absorption indicates that two distinct physical mechanisms are responsible for the grating formation. Weak, easily thermally bleached gratings resulted from exposure fluences below 0.3 kJ/cm2. Optical absorption measurements suggest that these low fluence gratings are predominantly absorption gratings. More thermally stable gratings, found to be refractive index gratings with unsaturated refractive index modulation amplitude as large as 6×10−5 were formed at cumulative fluences of 1 kJ/cm2 and above.


OSA Publishing

Peer Review: 

Published in Peer Reviewed Journal

Faculty Name: 

Faculty of Engineering and Design

Department Name: 

Department of Electronics

Items in CURVE are protected by copyright, with all rights reserved, unless otherwise indicated. They are made available with permission from the author(s).